NANOMET ROOF SHEET is the main cause of corrosion leakage

industrial metal roofing

NANOMET ROOF SHEET, as a building material, is widely used in industrial plants, animal husbandry, warehouse construction and so on. Once corrosion leakage occurs, it will cause certain economic losses! So how to avoid the corrosion of products? Below for you to analyze the causes of corrosion leakage and how to solve!

old metal roofing

Main causes of corrosion leakage in NANOMET ROOF SHEET:
1, the production and transportation process, the construction process caused by careless deformation of caigang tile.
2, wind, rain and other external forces, resulting in a long time of vibration of color steel tile roof, nail hole and iron seam long time of wear, rain rust, and then wear and rust, more and more serious.

zinc metal roof

3, NANOMET ROOF SHEET self-tapping nail with rubber pad why water seepage? First: the construction of self-tapping nails too hard has destroyed the rubber pad. Second: rubber pad aging fast, soon lost the waterproof effect.
4, high and low across the roof wall foot water penetration: the use of cement wipe eight Angle, sealant or waterproof coil waterproof protection. Cement and metal do not combine cracks, roll or sealant elongation is small will also appear larger cracks.